AISI 304L Stainless Steel vs. 86.5-silver 13.5-cadmium-oxide

AISI 304L stainless steel belongs to the iron alloys classification, while 86.5-silver 13.5-cadmium-oxide belongs to the otherwise unclassified metals. There are 8 material properties with values for both materials. Properties with values for just one material (27, in this case) are not shown.

For each property being compared, the top bar is AISI 304L stainless steel and the bottom bar is 86.5-silver 13.5-cadmium-oxide.

Metric UnitsUS Customary Units

Material Properties

Density, g/cm3 7.8
10
Electrical Conductivity: Equal Volume, % IACS 2.4
72 to 85
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
64 to 76
Elongation at Break, % 6.7 to 46
3.4 to 16
Shear Strength, MPa 370 to 680
170 to 210
Strength to Weight: Axial, points 19 to 41
7.6 to 11
Strength to Weight: Bending, points 19 to 31
9.3 to 12
Tensile Strength: Ultimate (UTS), MPa 540 to 1160
280 to 410