Annealed AISI 304L vs. Annealed 86.5-silver 13.5-cadmium-oxide
Annealed AISI 304L belongs to the iron alloys classification, while annealed 86.5-silver 13.5-cadmium-oxide belongs to the otherwise unclassified metals. There are 8 material properties with values for both materials. Properties with values for just one material (28, in this case) are not shown.
For each property being compared, the top bar is annealed AISI 304L and the bottom bar is annealed 86.5-silver 13.5-cadmium-oxide.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 7.8 | |
| 10 |
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 85 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.7 | |
| 76 |
| Elongation at Break, % | 42 | |
| 16 |
| Shear Strength, MPa | 370 | |
| 170 |
| Strength to Weight: Axial, points | 19 | |
| 7.6 |
| Strength to Weight: Bending, points | 19 | |
| 9.3 |
| Tensile Strength: Ultimate (UTS), MPa | 540 | |
| 280 |