AISI 304L Stainless Steel vs. EN 1.0034 Steel

Both AISI 304L stainless steel and EN 1.0034 steel are iron alloys. They have 70% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AISI 304L stainless steel and the bottom bar is EN 1.0034 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160 to 350
97 to 110
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 6.7 to 46
9.0 to 32
Fatigue Strength, MPa 170 to 430
140 to 170
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Shear Strength, MPa 370 to 680
220 to 230
Tensile Strength: Ultimate (UTS), MPa 540 to 1160
340 to 380
Tensile Strength: Yield (Proof), MPa 190 to 870
180 to 280

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 540
400
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 16
53
Thermal Expansion, µm/m-K 17
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 16
1.8
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.1
1.4
Embodied Energy, MJ/kg 44
18
Embodied Water, L/kg 150
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 71 to 240
31 to 95
Resilience: Unit (Modulus of Resilience), kJ/m3 92 to 1900
84 to 210
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 19 to 41
12 to 13
Strength to Weight: Bending, points 19 to 31
14 to 15
Thermal Diffusivity, mm2/s 4.2
14
Thermal Shock Resistance, points 12 to 25
11 to 12

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.15
Chromium (Cr), % 18 to 20
0
Iron (Fe), % 65 to 74
98.7 to 100
Manganese (Mn), % 0 to 2.0
0 to 0.7
Nickel (Ni), % 8.0 to 12
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.045
Silicon (Si), % 0 to 0.75
0 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.045

Comparable Variants