AISI 304L Stainless Steel vs. SAE-AISI 1065 Steel

Both AISI 304L stainless steel and SAE-AISI 1065 steel are iron alloys. They have 70% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is AISI 304L stainless steel and the bottom bar is SAE-AISI 1065 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160 to 350
210 to 230
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 6.7 to 46
11 to 14
Fatigue Strength, MPa 170 to 430
270 to 340
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
72
Shear Strength, MPa 370 to 680
430 to 470
Tensile Strength: Ultimate (UTS), MPa 540 to 1160
710 to 780
Tensile Strength: Yield (Proof), MPa 190 to 870
430 to 550

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 540
400
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 16
51
Thermal Expansion, µm/m-K 17
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
11
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
12

Otherwise Unclassified Properties

Base Metal Price, % relative 16
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.1
1.4
Embodied Energy, MJ/kg 44
19
Embodied Water, L/kg 150
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 71 to 240
74 to 90
Resilience: Unit (Modulus of Resilience), kJ/m3 92 to 1900
490 to 820
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 19 to 41
25 to 28
Strength to Weight: Bending, points 19 to 31
23 to 24
Thermal Diffusivity, mm2/s 4.2
14
Thermal Shock Resistance, points 12 to 25
25 to 27

Alloy Composition

Carbon (C), % 0 to 0.030
0.6 to 0.7
Chromium (Cr), % 18 to 20
0
Iron (Fe), % 65 to 74
98.3 to 98.8
Manganese (Mn), % 0 to 2.0
0.6 to 0.9
Nickel (Ni), % 8.0 to 12
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 0.75
0
Sulfur (S), % 0 to 0.030
0 to 0.050

Comparable Variants