AISI 304L Stainless Steel vs. SAE-AISI S5 Steel

Both AISI 304L stainless steel and SAE-AISI S5 steel are iron alloys. They have 71% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is AISI 304L stainless steel and the bottom bar is SAE-AISI S5 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
72
Tensile Strength: Ultimate (UTS), MPa 540 to 1160
680 to 1940

Thermal Properties

Latent Heat of Fusion, J/g 290
280
Melting Completion (Liquidus), °C 1450
1440
Melting Onset (Solidus), °C 1400
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 16
42
Thermal Expansion, µm/m-K 17
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 16
3.1
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 3.1
2.1
Embodied Energy, MJ/kg 44
29
Embodied Water, L/kg 150
51

Common Calculations

PREN (Pitting Resistance) 20
2.9
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 19 to 41
25 to 70
Strength to Weight: Bending, points 19 to 31
22 to 45
Thermal Diffusivity, mm2/s 4.2
11
Thermal Shock Resistance, points 12 to 25
23 to 65

Alloy Composition

Carbon (C), % 0 to 0.030
0.5 to 0.65
Chromium (Cr), % 18 to 20
0 to 0.5
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 65 to 74
93.6 to 97
Manganese (Mn), % 0 to 2.0
0.6 to 1.0
Molybdenum (Mo), % 0
0.2 to 1.4
Nickel (Ni), % 8.0 to 12
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.030
Silicon (Si), % 0 to 0.75
1.8 to 2.3
Sulfur (S), % 0 to 0.030
0 to 0.030
Vanadium (V), % 0
0 to 0.35

Comparable Variants