SAE-AISI S5 (T41905) Shock-Resisting Steel

SAE-AISI S5 steel is a tool steel. S5 is the designation in both the SAE and AISI systems for this material. T41905 is the UNS number.

The properties of SAE-AISI S5 steel include two common variations. This page shows summary ranges across both of them. For more specific values, follow the links immediately below. The graph bars on the material properties cards further below compare SAE-AISI S5 steel to: tool steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Elastic (Young's, Tensile) Modulus

190 GPa 27 x 106 psi

Poisson's Ratio

0.29

Shear Modulus

72 GPa 10 x 106 psi

Tensile Strength: Ultimate (UTS)

680 to 1940 MPa 99 to 280 x 103 psi

Thermal Properties

Latent Heat of Fusion

280 J/g

Melting Completion (Liquidus)

1440 °C 2620 °F

Melting Onset (Solidus)

1400 °C 2550 °F

Specific Heat Capacity

480 J/kg-K 0.11 BTU/lb-°F

Thermal Conductivity

42 W/m-K 24 BTU/h-ft-°F

Thermal Expansion

12 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

7.4 % IACS

Electrical Conductivity: Equal Weight (Specific)

8.7 % IACS

Otherwise Unclassified Properties

Base Metal Price

3.1 % relative

Density

7.7 g/cm3 480 lb/ft3

Embodied Carbon

2.1 kg CO2/kg material

Embodied Energy

29 MJ/kg 12 x 103 BTU/lb

Embodied Water

51 L/kg 6.0 gal/lb

Common Calculations

PREN (Pitting Resistance)

2.9

Stiffness to Weight: Axial

13 points

Stiffness to Weight: Bending

25 points

Strength to Weight: Axial

25 to 70 points

Strength to Weight: Bending

22 to 45 points

Thermal Diffusivity

11 mm2/s

Thermal Shock Resistance

23 to 65 points

Alloy Composition

Iron (Fe) 93.6 to 97
Silicon (Si) 1.8 to 2.3
Manganese (Mn) 0.6 to 1.0
Molybdenum (Mo) 0.2 to 1.4
Carbon (C) 0.5 to 0.65
Chromium (Cr) 0 to 0.5
Vanadium (V) 0 to 0.35
Copper (Cu) 0 to 0.25
Phosphorus (P) 0 to 0.030
Sulfur (S) 0 to 0.030

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Similar Alloys

Further Reading

SAE J437: Selection and Heat Treatment of Tool and Die Steels

ASTM A681: Standard Specification for Tool Steels Alloy

Tool Steels, 5th ed., George Roberts et al., 1998

Tool Steels: Properties and Performance, Rafael A. Mesquita (editor), 2016

ASM Specialty Handbook: Carbon and Alloy Steels, J. R. Davis (editor), 1996