AISI 310 Stainless Steel vs. EN 1.4006 Stainless Steel

Both AISI 310 stainless steel and EN 1.4006 stainless steel are iron alloys. They have 67% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is AISI 310 stainless steel and the bottom bar is EN 1.4006 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34 to 45
16 to 23
Fatigue Strength, MPa 240 to 280
150 to 300
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 78
76
Shear Strength, MPa 420 to 470
370 to 460
Tensile Strength: Ultimate (UTS), MPa 600 to 710
590 to 750
Tensile Strength: Yield (Proof), MPa 260 to 350
230 to 510

Thermal Properties

Latent Heat of Fusion, J/g 310
270
Maximum Temperature: Corrosion, °C 440
390
Maximum Temperature: Mechanical, °C 1040
740
Melting Completion (Liquidus), °C 1450
1440
Melting Onset (Solidus), °C 1400
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
30
Thermal Expansion, µm/m-K 15
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 25
7.0
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 4.3
1.9
Embodied Energy, MJ/kg 61
27
Embodied Water, L/kg 190
100

Common Calculations

PREN (Pitting Resistance) 25
13
Resilience: Ultimate (Unit Rupture Work), MJ/m3 200 to 220
99 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 170 to 310
140 to 660
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21 to 25
21 to 27
Strength to Weight: Bending, points 20 to 22
20 to 24
Thermal Diffusivity, mm2/s 3.9
8.1
Thermal Shock Resistance, points 14 to 17
21 to 26

Alloy Composition

Carbon (C), % 0 to 0.25
0.080 to 0.15
Chromium (Cr), % 24 to 26
11.5 to 13.5
Iron (Fe), % 48.2 to 57
83.1 to 88.4
Manganese (Mn), % 0 to 2.0
0 to 1.5
Nickel (Ni), % 19 to 22
0 to 0.75
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015

Comparable Variants