AISI 310Cb Stainless Steel vs. Grade VDSiCrV Steel

Both AISI 310Cb stainless steel and grade VDSiCrV steel are iron alloys. They have 54% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AISI 310Cb stainless steel and the bottom bar is grade VDSiCrV steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
630
Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Reduction in Area, % 46
48
Shear Modulus, GPa 78
80
Tensile Strength: Ultimate (UTS), MPa 580
2100

Thermal Properties

Latent Heat of Fusion, J/g 310
270
Maximum Temperature: Mechanical, °C 1100
420
Melting Completion (Liquidus), °C 1410
1440
Melting Onset (Solidus), °C 1360
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
47
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 28
2.3
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 4.8
1.9
Embodied Energy, MJ/kg 69
26
Embodied Water, L/kg 190
50

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 20
75
Strength to Weight: Bending, points 20
47
Thermal Diffusivity, mm2/s 3.9
13
Thermal Shock Resistance, points 13
63

Alloy Composition

Carbon (C), % 0 to 0.080
0.5 to 0.7
Chromium (Cr), % 24 to 26
0.5 to 1.0
Copper (Cu), % 0
0 to 0.060
Iron (Fe), % 47.2 to 57
96.1 to 97.8
Manganese (Mn), % 0 to 2.0
0.4 to 0.9
Nickel (Ni), % 19 to 22
0
Niobium (Nb), % 0 to 1.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.020
Silicon (Si), % 0 to 1.5
1.2 to 1.7
Sulfur (S), % 0 to 0.030
0 to 0.020
Vanadium (V), % 0
0.1 to 0.25