AISI 310H Stainless Steel vs. EN 1.0345 Steel

Both AISI 310H stainless steel and EN 1.0345 steel are iron alloys. They have 55% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is AISI 310H stainless steel and the bottom bar is EN 1.0345 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
120
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 40
27
Fatigue Strength, MPa 200
170
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 79
73
Shear Strength, MPa 400
270
Tensile Strength: Ultimate (UTS), MPa 580
420
Tensile Strength: Yield (Proof), MPa 230
230

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1410
1460
Melting Onset (Solidus), °C 1360
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
49
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 25
2.1
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 4.3
1.5
Embodied Energy, MJ/kg 61
19
Embodied Water, L/kg 190
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
96
Resilience: Unit (Modulus of Resilience), kJ/m3 130
140
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
15
Strength to Weight: Bending, points 20
16
Thermal Diffusivity, mm2/s 3.9
13
Thermal Shock Resistance, points 13
13

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.024
Carbon (C), % 0.040 to 0.1
0 to 0.16
Chromium (Cr), % 24 to 26
0 to 0.3
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 49.1 to 57
97.2 to 99.38
Manganese (Mn), % 0 to 2.0
0.6 to 1.2
Molybdenum (Mo), % 0
0 to 0.080
Nickel (Ni), % 19 to 22
0 to 0.3
Niobium (Nb), % 0
0 to 0.020
Nitrogen (N), % 0
0 to 0.012
Phosphorus (P), % 0 to 0.045
0 to 0.025
Silicon (Si), % 0 to 0.75
0 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.010
Titanium (Ti), % 0
0 to 0.030
Vanadium (V), % 0
0 to 0.020