AISI 310MoLN Stainless Steel vs. ASTM A182 Grade FR

Both AISI 310MoLN stainless steel and ASTM A182 grade FR are iron alloys. Both are furnished in the annealed condition. They have 52% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is AISI 310MoLN stainless steel and the bottom bar is ASTM A182 grade FR.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
170
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 28
28
Fatigue Strength, MPa 210
270
Poisson's Ratio 0.28
0.29
Reduction in Area, % 45
43
Shear Modulus, GPa 80
72
Shear Strength, MPa 400
320
Tensile Strength: Ultimate (UTS), MPa 610
490
Tensile Strength: Yield (Proof), MPa 290
360

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
410
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 14
52
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 28
3.3
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 5.0
1.6
Embodied Energy, MJ/kg 70
21
Embodied Water, L/kg 200
52

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
120
Resilience: Unit (Modulus of Resilience), kJ/m3 200
340
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
17
Strength to Weight: Bending, points 20
17
Thermal Diffusivity, mm2/s 3.7
14
Thermal Shock Resistance, points 14
14

Alloy Composition

Carbon (C), % 0 to 0.020
0 to 0.2
Chromium (Cr), % 24 to 26
0
Copper (Cu), % 0
0.75 to 1.3
Iron (Fe), % 45.2 to 53.8
95.2 to 97.3
Manganese (Mn), % 0 to 2.0
0.4 to 1.1
Molybdenum (Mo), % 1.6 to 2.6
0
Nickel (Ni), % 20.5 to 23.5
1.6 to 2.2
Nitrogen (N), % 0.090 to 0.15
0
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 0 to 0.5
0
Sulfur (S), % 0 to 0.010
0 to 0.050