AISI 310MoLN Stainless Steel vs. ASTM Grade HE Steel

Both AISI 310MoLN stainless steel and ASTM grade HE steel are iron alloys. They have 86% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is AISI 310MoLN stainless steel and the bottom bar is ASTM grade HE steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
190
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 28
10
Fatigue Strength, MPa 210
160
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 80
79
Tensile Strength: Ultimate (UTS), MPa 610
670
Tensile Strength: Yield (Proof), MPa 290
310

Thermal Properties

Latent Heat of Fusion, J/g 300
310
Maximum Temperature: Corrosion, °C 450
450
Maximum Temperature: Mechanical, °C 1100
1100
Melting Completion (Liquidus), °C 1420
1400
Melting Onset (Solidus), °C 1380
1360
Specific Heat Capacity, J/kg-K 470
490
Thermal Conductivity, W/m-K 14
14
Thermal Expansion, µm/m-K 16
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 28
19
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 5.0
3.5
Embodied Energy, MJ/kg 70
50
Embodied Water, L/kg 200
190

Common Calculations

PREN (Pitting Resistance) 34
29
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
56
Resilience: Unit (Modulus of Resilience), kJ/m3 200
240
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21
24
Strength to Weight: Bending, points 20
22
Thermal Diffusivity, mm2/s 3.7
3.6
Thermal Shock Resistance, points 14
14

Alloy Composition

Carbon (C), % 0 to 0.020
0.2 to 0.5
Chromium (Cr), % 24 to 26
26 to 30
Iron (Fe), % 45.2 to 53.8
53.9 to 65.8
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 1.6 to 2.6
0 to 0.5
Nickel (Ni), % 20.5 to 23.5
8.0 to 11
Nitrogen (N), % 0.090 to 0.15
0
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.5
0 to 2.0
Sulfur (S), % 0 to 0.010
0 to 0.040