AISI 310MoLN Stainless Steel vs. S33228 Stainless Steel

Both AISI 310MoLN stainless steel and S33228 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 87% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AISI 310MoLN stainless steel and the bottom bar is S33228 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
190
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 28
34
Fatigue Strength, MPa 210
170
Poisson's Ratio 0.28
0.28
Reduction in Area, % 45
39
Rockwell B Hardness 84
82
Shear Modulus, GPa 80
79
Shear Strength, MPa 400
380
Tensile Strength: Ultimate (UTS), MPa 610
570
Tensile Strength: Yield (Proof), MPa 290
210

Thermal Properties

Latent Heat of Fusion, J/g 300
310
Maximum Temperature: Corrosion, °C 450
560
Maximum Temperature: Mechanical, °C 1100
1100
Melting Completion (Liquidus), °C 1420
1410
Melting Onset (Solidus), °C 1380
1360
Specific Heat Capacity, J/kg-K 470
470
Thermal Expansion, µm/m-K 16
16

Otherwise Unclassified Properties

Base Metal Price, % relative 28
37
Density, g/cm3 7.9
8.0
Embodied Carbon, kg CO2/kg material 5.0
6.2
Embodied Energy, MJ/kg 70
89
Embodied Water, L/kg 200
220

Common Calculations

PREN (Pitting Resistance) 34
27
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
150
Resilience: Unit (Modulus of Resilience), kJ/m3 200
110
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
20
Strength to Weight: Bending, points 20
19
Thermal Shock Resistance, points 14
13

Alloy Composition

Aluminum (Al), % 0
0 to 0.025
Carbon (C), % 0 to 0.020
0.040 to 0.080
Cerium (Ce), % 0
0.050 to 0.1
Chromium (Cr), % 24 to 26
26 to 28
Iron (Fe), % 45.2 to 53.8
36.5 to 42.3
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 1.6 to 2.6
0
Nickel (Ni), % 20.5 to 23.5
31 to 33
Niobium (Nb), % 0
0.6 to 1.0
Nitrogen (N), % 0.090 to 0.15
0
Phosphorus (P), % 0 to 0.030
0 to 0.020
Silicon (Si), % 0 to 0.5
0 to 0.3
Sulfur (S), % 0 to 0.010
0 to 0.015