AISI 310S Stainless Steel vs. 356.0 Aluminum

AISI 310S stainless steel belongs to the iron alloys classification, while 356.0 aluminum belongs to the aluminum alloys. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AISI 310S stainless steel and the bottom bar is 356.0 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170 to 210
55 to 75
Elastic (Young's, Tensile) Modulus, GPa 200
70
Elongation at Break, % 34 to 44
2.0 to 3.8
Fatigue Strength, MPa 250 to 280
55 to 75
Poisson's Ratio 0.27
0.33
Shear Modulus, GPa 79
27
Shear Strength, MPa 420 to 470
140 to 190
Tensile Strength: Ultimate (UTS), MPa 600 to 710
160 to 240
Tensile Strength: Yield (Proof), MPa 270 to 350
100 to 190

Thermal Properties

Latent Heat of Fusion, J/g 310
500
Maximum Temperature: Mechanical, °C 1100
170
Melting Completion (Liquidus), °C 1450
620
Melting Onset (Solidus), °C 1400
570
Specific Heat Capacity, J/kg-K 480
900
Thermal Conductivity, W/m-K 16
150 to 170
Thermal Expansion, µm/m-K 16
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
40 to 43
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
140 to 150

Otherwise Unclassified Properties

Base Metal Price, % relative 25
9.5
Density, g/cm3 7.9
2.6
Embodied Carbon, kg CO2/kg material 4.3
8.0
Embodied Energy, MJ/kg 61
150
Embodied Water, L/kg 190
1110

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 200 to 220
3.2 to 8.2
Resilience: Unit (Modulus of Resilience), kJ/m3 190 to 310
70 to 250
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 25
53
Strength to Weight: Axial, points 21 to 25
17 to 26
Strength to Weight: Bending, points 20 to 22
25 to 33
Thermal Diffusivity, mm2/s 4.1
64 to 71
Thermal Shock Resistance, points 14 to 16
7.6 to 11

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
90.1 to 93.3
Carbon (C), % 0 to 0.080
0
Chromium (Cr), % 24 to 26
0
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 48.3 to 57
0 to 0.6
Magnesium (Mg), % 0
0.2 to 0.45
Manganese (Mn), % 0 to 2.0
0 to 0.35
Nickel (Ni), % 19 to 22
0
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0 to 1.5
6.5 to 7.5
Sulfur (S), % 0 to 0.030
0
Titanium (Ti), % 0
0 to 0.25
Zinc (Zn), % 0
0 to 0.35
Residuals, % 0
0 to 0.15