AISI 310S Stainless Steel vs. Ductile Cast Iron

Both AISI 310S stainless steel and ductile cast iron are iron alloys. They have 53% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AISI 310S stainless steel and the bottom bar is ductile cast iron.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170 to 210
160 to 310
Elastic (Young's, Tensile) Modulus, GPa 200
170 to 180
Elongation at Break, % 34 to 44
2.1 to 20
Poisson's Ratio 0.27
0.28 to 0.31
Shear Modulus, GPa 79
64 to 70
Shear Strength, MPa 420 to 470
420 to 800
Tensile Strength: Ultimate (UTS), MPa 600 to 710
460 to 920
Tensile Strength: Yield (Proof), MPa 270 to 350
310 to 670

Thermal Properties

Latent Heat of Fusion, J/g 310
270
Maximum Temperature: Mechanical, °C 1100
290
Melting Completion (Liquidus), °C 1450
1160
Melting Onset (Solidus), °C 1400
1120
Specific Heat Capacity, J/kg-K 480
490
Thermal Conductivity, W/m-K 16
31 to 36
Thermal Expansion, µm/m-K 16
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
8.8 to 9.4

Otherwise Unclassified Properties

Base Metal Price, % relative 25
1.9
Density, g/cm3 7.9
7.1 to 7.5
Embodied Carbon, kg CO2/kg material 4.3
1.5
Embodied Energy, MJ/kg 61
21
Embodied Water, L/kg 190
43

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 200 to 220
17 to 80
Resilience: Unit (Modulus of Resilience), kJ/m3 190 to 310
280 to 1330
Stiffness to Weight: Axial, points 14
12 to 14
Stiffness to Weight: Bending, points 25
24 to 26
Strength to Weight: Axial, points 21 to 25
17 to 35
Strength to Weight: Bending, points 20 to 22
18 to 29
Thermal Diffusivity, mm2/s 4.1
8.9 to 10
Thermal Shock Resistance, points 14 to 16
17 to 35

Alloy Composition

Carbon (C), % 0 to 0.080
3.0 to 3.5
Chromium (Cr), % 24 to 26
0
Iron (Fe), % 48.3 to 57
93.7 to 95.5
Manganese (Mn), % 0 to 2.0
0
Nickel (Ni), % 19 to 22
0
Phosphorus (P), % 0 to 0.045
0 to 0.080
Silicon (Si), % 0 to 1.5
1.5 to 2.8
Sulfur (S), % 0 to 0.030
0

Comparable Variants