AISI 310S Stainless Steel vs. C94900 Bronze

AISI 310S stainless steel belongs to the iron alloys classification, while C94900 bronze belongs to the copper alloys. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AISI 310S stainless steel and the bottom bar is C94900 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
110
Elongation at Break, % 34 to 44
17
Poisson's Ratio 0.27
0.34
Shear Modulus, GPa 79
41
Tensile Strength: Ultimate (UTS), MPa 600 to 710
300
Tensile Strength: Yield (Proof), MPa 270 to 350
130

Thermal Properties

Latent Heat of Fusion, J/g 310
190
Maximum Temperature: Mechanical, °C 1100
170
Melting Completion (Liquidus), °C 1450
980
Melting Onset (Solidus), °C 1400
910
Specific Heat Capacity, J/kg-K 480
370
Thermal Expansion, µm/m-K 16
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
14
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
14

Otherwise Unclassified Properties

Base Metal Price, % relative 25
32
Density, g/cm3 7.9
8.8
Embodied Carbon, kg CO2/kg material 4.3
3.4
Embodied Energy, MJ/kg 61
55
Embodied Water, L/kg 190
350

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 200 to 220
41
Resilience: Unit (Modulus of Resilience), kJ/m3 190 to 310
72
Stiffness to Weight: Axial, points 14
6.9
Stiffness to Weight: Bending, points 25
18
Strength to Weight: Axial, points 21 to 25
9.4
Strength to Weight: Bending, points 20 to 22
11
Thermal Shock Resistance, points 14 to 16
11

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
0 to 0.0050
Antimony (Sb), % 0
0 to 0.25
Carbon (C), % 0 to 0.080
0
Chromium (Cr), % 24 to 26
0
Copper (Cu), % 0
79 to 81
Iron (Fe), % 48.3 to 57
0 to 0.3
Lead (Pb), % 0
4.0 to 6.0
Manganese (Mn), % 0 to 2.0
0 to 0.1
Nickel (Ni), % 19 to 22
4.0 to 6.0
Phosphorus (P), % 0 to 0.045
0 to 0.050
Silicon (Si), % 0 to 1.5
0 to 0.0050
Sulfur (S), % 0 to 0.030
0 to 0.080
Tin (Sn), % 0
4.0 to 6.0
Zinc (Zn), % 0
4.0 to 6.0
Residuals, % 0
0 to 0.8