AISI 410 Stainless Steel vs. SAE-AISI 1541 Steel
Both AISI 410 stainless steel and SAE-AISI 1541 steel are iron alloys. They have 87% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is AISI 410 stainless steel and the bottom bar is SAE-AISI 1541 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 190 to 240 | |
210 to 220 |
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
190 |
Elongation at Break, % | 16 to 22 | |
11 to 17 |
Fatigue Strength, MPa | 190 to 350 | |
260 to 420 |
Poisson's Ratio | 0.28 | |
0.29 |
Reduction in Area, % | 47 to 48 | |
34 to 51 |
Shear Modulus, GPa | 76 | |
73 |
Shear Strength, MPa | 330 to 470 | |
440 to 480 |
Tensile Strength: Ultimate (UTS), MPa | 520 to 770 | |
720 to 790 |
Tensile Strength: Yield (Proof), MPa | 290 to 580 | |
390 to 680 |
Thermal Properties
Latent Heat of Fusion, J/g | 270 | |
250 |
Maximum Temperature: Mechanical, °C | 710 | |
400 |
Melting Completion (Liquidus), °C | 1530 | |
1460 |
Melting Onset (Solidus), °C | 1480 | |
1420 |
Specific Heat Capacity, J/kg-K | 480 | |
470 |
Thermal Conductivity, W/m-K | 30 | |
52 |
Thermal Expansion, µm/m-K | 11 | |
12 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 2.9 | |
7.1 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 3.3 | |
8.2 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 7.0 | |
1.9 |
Density, g/cm3 | 7.7 | |
7.8 |
Embodied Carbon, kg CO2/kg material | 1.9 | |
1.4 |
Embodied Energy, MJ/kg | 27 | |
19 |
Embodied Water, L/kg | 100 | |
48 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 97 to 110 | |
78 to 100 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 210 to 860 | |
410 to 1250 |
Stiffness to Weight: Axial, points | 14 | |
13 |
Stiffness to Weight: Bending, points | 25 | |
24 |
Strength to Weight: Axial, points | 19 to 28 | |
25 to 28 |
Strength to Weight: Bending, points | 19 to 24 | |
23 to 24 |
Thermal Diffusivity, mm2/s | 8.1 | |
14 |
Thermal Shock Resistance, points | 18 to 26 | |
23 to 25 |
Alloy Composition
Carbon (C), % | 0.080 to 0.15 | |
0.36 to 0.44 |
Chromium (Cr), % | 11.5 to 13.5 | |
0 |
Iron (Fe), % | 83.5 to 88.4 | |
97.8 to 98.3 |
Manganese (Mn), % | 0 to 1.0 | |
1.4 to 1.7 |
Nickel (Ni), % | 0 to 0.75 | |
0 |
Phosphorus (P), % | 0 to 0.040 | |
0 to 0.040 |
Silicon (Si), % | 0 to 1.0 | |
0 |
Sulfur (S), % | 0 to 0.030 | |
0 to 0.050 |