AISI 414 Stainless Steel vs. EN 1.5535 Steel

Both AISI 414 stainless steel and EN 1.5535 steel are iron alloys. They have 85% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is AISI 414 stainless steel and the bottom bar is EN 1.5535 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 17
11 to 22
Fatigue Strength, MPa 430 to 480
210 to 320
Poisson's Ratio 0.28
0.29
Reduction in Area, % 50
62 to 72
Shear Modulus, GPa 76
73
Shear Strength, MPa 550 to 590
320 to 370
Tensile Strength: Ultimate (UTS), MPa 900 to 960
450 to 1490
Tensile Strength: Yield (Proof), MPa 700 to 790
300 to 500

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 750
400
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 25
50
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.9
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 8.0
1.9
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.1
1.4
Embodied Energy, MJ/kg 29
19
Embodied Water, L/kg 100
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140 to 150
45 to 250
Resilience: Unit (Modulus of Resilience), kJ/m3 1260 to 1590
240 to 680
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 32 to 34
16 to 53
Strength to Weight: Bending, points 27 to 28
17 to 37
Thermal Diffusivity, mm2/s 6.7
13
Thermal Shock Resistance, points 33 to 35
13 to 44

Alloy Composition

Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 0 to 0.15
0.2 to 0.25
Chromium (Cr), % 11.5 to 13.5
0 to 0.3
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 81.8 to 87.3
97.6 to 98.9
Manganese (Mn), % 0 to 1.0
0.9 to 1.2
Nickel (Ni), % 1.3 to 2.5
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.3
Sulfur (S), % 0 to 0.030
0 to 0.025

Comparable Variants