AISI 416 Stainless Steel vs. ACI-ASTM CG6MMN Steel
Both AISI 416 stainless steel and ACI-ASTM CG6MMN steel are iron alloys. They have 71% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is AISI 416 stainless steel and the bottom bar is ACI-ASTM CG6MMN steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 230 to 320 | |
| 190 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 13 to 31 | |
| 34 |
| Fatigue Strength, MPa | 230 to 340 | |
| 260 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 76 | |
| 79 |
| Tensile Strength: Ultimate (UTS), MPa | 510 to 800 | |
| 670 |
| Tensile Strength: Yield (Proof), MPa | 290 to 600 | |
| 320 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 300 |
| Maximum Temperature: Corrosion, °C | 390 | |
| 460 |
| Maximum Temperature: Mechanical, °C | 680 | |
| 1080 |
| Melting Completion (Liquidus), °C | 1530 | |
| 1420 |
| Melting Onset (Solidus), °C | 1480 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 480 |
| Thermal Expansion, µm/m-K | 9.9 | |
| 17 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 7.0 | |
| 22 |
| Density, g/cm3 | 7.7 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.9 | |
| 4.8 |
| Embodied Energy, MJ/kg | 27 | |
| 68 |
| Embodied Water, L/kg | 100 | |
| 180 |
Common Calculations
| PREN (Pitting Resistance) | 13 | |
| 34 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 98 to 140 | |
| 190 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 220 to 940 | |
| 260 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 18 to 29 | |
| 24 |
| Strength to Weight: Bending, points | 18 to 25 | |
| 22 |
| Thermal Shock Resistance, points | 19 to 30 | |
| 14 |
Alloy Composition
| Carbon (C), % | 0 to 0.15 | |
| 0 to 0.060 |
| Chromium (Cr), % | 12 to 14 | |
| 20.5 to 23.5 |
| Iron (Fe), % | 83.2 to 87.9 | |
| 51.9 to 62.1 |
| Manganese (Mn), % | 0 to 1.3 | |
| 4.0 to 6.0 |
| Molybdenum (Mo), % | 0 | |
| 1.5 to 3.0 |
| Nickel (Ni), % | 0 | |
| 11.5 to 13.5 |
| Niobium (Nb), % | 0 | |
| 0.1 to 0.3 |
| Nitrogen (N), % | 0 | |
| 0.2 to 0.4 |
| Phosphorus (P), % | 0 to 0.060 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0.15 to 0.35 | |
| 0 to 0.030 |
| Vanadium (V), % | 0 | |
| 0.1 to 0.3 |