AISI 416 Stainless Steel vs. Austenitic Grey Cast Iron

Both AISI 416 stainless steel and austenitic grey cast iron are iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is AISI 416 stainless steel and the bottom bar is austenitic grey cast iron.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 230 to 320
110 to 210
Elastic (Young's, Tensile) Modulus, GPa 190
180
Poisson's Ratio 0.28
0.29 to 0.3
Shear Modulus, GPa 76
69 to 72
Tensile Strength: Ultimate (UTS), MPa 510 to 800
150 to 230

Thermal Properties

Latent Heat of Fusion, J/g 270
280 to 350
Melting Completion (Liquidus), °C 1530
1340 to 1400
Melting Onset (Solidus), °C 1480
1290 to 1350
Specific Heat Capacity, J/kg-K 480
470 to 490
Thermal Expansion, µm/m-K 9.9
13 to 14

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
14 to 24
Density, g/cm3 7.7
7.7 to 8.1
Embodied Carbon, kg CO2/kg material 1.9
3.1 to 4.7
Embodied Energy, MJ/kg 27
43 to 65
Embodied Water, L/kg 100
93 to 120

Common Calculations

PREN (Pitting Resistance) 13
2.0 to 5.0
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
23 to 25
Strength to Weight: Axial, points 18 to 29
5.3 to 8.2
Strength to Weight: Bending, points 18 to 25
7.9 to 11
Thermal Shock Resistance, points 19 to 30
4.5 to 6.5