AISI 416 Stainless Steel vs. EN 1.1118 Cast Steel

Both AISI 416 stainless steel and EN 1.1118 cast steel are iron alloys. They have 87% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AISI 416 stainless steel and the bottom bar is EN 1.1118 cast steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 13 to 31
14 to 21
Fatigue Strength, MPa 230 to 340
320 to 400
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Tensile Strength: Ultimate (UTS), MPa 510 to 800
700 to 750
Tensile Strength: Yield (Proof), MPa 290 to 600
460 to 630

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Maximum Temperature: Mechanical, °C 680
400
Melting Completion (Liquidus), °C 1530
1460
Melting Onset (Solidus), °C 1480
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 30
51
Thermal Expansion, µm/m-K 9.9
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
1.9
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 1.9
1.4
Embodied Energy, MJ/kg 27
19
Embodied Water, L/kg 100
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 98 to 140
97 to 130
Resilience: Unit (Modulus of Resilience), kJ/m3 220 to 940
550 to 1050
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 18 to 29
25 to 27
Strength to Weight: Bending, points 18 to 25
22 to 23
Thermal Diffusivity, mm2/s 8.1
14
Thermal Shock Resistance, points 19 to 30
22 to 24

Alloy Composition

Carbon (C), % 0 to 0.15
0.2 to 0.25
Chromium (Cr), % 12 to 14
0
Iron (Fe), % 83.2 to 87.9
97.3 to 98.3
Manganese (Mn), % 0 to 1.3
1.5 to 1.8
Phosphorus (P), % 0 to 0.060
0 to 0.020
Silicon (Si), % 0 to 1.0
0 to 0.6
Sulfur (S), % 0.15 to 0.35
0 to 0.015