AISI 416 Stainless Steel vs. EN 1.1152 Steel

Both AISI 416 stainless steel and EN 1.1152 steel are iron alloys. They have 86% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is AISI 416 stainless steel and the bottom bar is EN 1.1152 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 230 to 320
120 to 160
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 13 to 31
12 to 22
Fatigue Strength, MPa 230 to 340
190 to 300
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 340 to 480
290 to 340
Tensile Strength: Ultimate (UTS), MPa 510 to 800
400 to 550
Tensile Strength: Yield (Proof), MPa 290 to 600
270 to 440

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Maximum Temperature: Mechanical, °C 680
400
Melting Completion (Liquidus), °C 1530
1460
Melting Onset (Solidus), °C 1480
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 30
52
Thermal Expansion, µm/m-K 9.9
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
1.8
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 1.9
1.4
Embodied Energy, MJ/kg 27
18
Embodied Water, L/kg 100
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 98 to 140
41 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 220 to 940
200 to 530
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 18 to 29
14 to 19
Strength to Weight: Bending, points 18 to 25
15 to 19
Thermal Diffusivity, mm2/s 8.1
14
Thermal Shock Resistance, points 19 to 30
13 to 17

Alloy Composition

Carbon (C), % 0 to 0.15
0.18 to 0.22
Chromium (Cr), % 12 to 14
0
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 83.2 to 87.9
98.6 to 99.52
Manganese (Mn), % 0 to 1.3
0.3 to 0.6
Phosphorus (P), % 0 to 0.060
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.3
Sulfur (S), % 0.15 to 0.35
0 to 0.025