AISI 416 Stainless Steel vs. EN 1.4910 Stainless Steel

Both AISI 416 stainless steel and EN 1.4910 stainless steel are iron alloys. They have 80% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is AISI 416 stainless steel and the bottom bar is EN 1.4910 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 230 to 320
200
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 13 to 31
41
Fatigue Strength, MPa 230 to 340
250
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
78
Shear Strength, MPa 340 to 480
450
Tensile Strength: Ultimate (UTS), MPa 510 to 800
650
Tensile Strength: Yield (Proof), MPa 290 to 600
290

Thermal Properties

Latent Heat of Fusion, J/g 270
290
Maximum Temperature: Corrosion, °C 390
410
Maximum Temperature: Mechanical, °C 680
950
Melting Completion (Liquidus), °C 1530
1440
Melting Onset (Solidus), °C 1480
1400
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 30
16
Thermal Expansion, µm/m-K 9.9
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
20
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 1.9
3.9
Embodied Energy, MJ/kg 27
54
Embodied Water, L/kg 100
150

Common Calculations

PREN (Pitting Resistance) 13
27
Resilience: Ultimate (Unit Rupture Work), MJ/m3 98 to 140
220
Resilience: Unit (Modulus of Resilience), kJ/m3 220 to 940
210
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 18 to 29
23
Strength to Weight: Bending, points 18 to 25
21
Thermal Diffusivity, mm2/s 8.1
4.3
Thermal Shock Resistance, points 19 to 30
14

Alloy Composition

Boron (B), % 0
0.0015 to 0.0050
Carbon (C), % 0 to 0.15
0 to 0.040
Chromium (Cr), % 12 to 14
16 to 18
Iron (Fe), % 83.2 to 87.9
62 to 69.9
Manganese (Mn), % 0 to 1.3
0 to 2.0
Molybdenum (Mo), % 0
2.0 to 3.0
Nickel (Ni), % 0
12 to 14
Nitrogen (N), % 0
0.1 to 0.18
Phosphorus (P), % 0 to 0.060
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 0.75
Sulfur (S), % 0.15 to 0.35
0 to 0.015