AISI 416 Stainless Steel vs. SAE-AISI 1026 Steel

Both AISI 416 stainless steel and SAE-AISI 1026 steel are iron alloys. They have 86% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is AISI 416 stainless steel and the bottom bar is SAE-AISI 1026 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 230 to 320
140 to 160
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 13 to 31
17 to 27
Fatigue Strength, MPa 230 to 340
200 to 310
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 340 to 480
320 to 340
Tensile Strength: Ultimate (UTS), MPa 510 to 800
500 to 550
Tensile Strength: Yield (Proof), MPa 290 to 600
270 to 470

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Maximum Temperature: Mechanical, °C 680
400
Melting Completion (Liquidus), °C 1530
1460
Melting Onset (Solidus), °C 1480
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 30
52
Thermal Expansion, µm/m-K 9.9
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
1.8
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 1.9
1.4
Embodied Energy, MJ/kg 27
18
Embodied Water, L/kg 100
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 98 to 140
89 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 220 to 940
200 to 580
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 18 to 29
18 to 20
Strength to Weight: Bending, points 18 to 25
18 to 19
Thermal Diffusivity, mm2/s 8.1
14
Thermal Shock Resistance, points 19 to 30
16 to 18

Alloy Composition

Carbon (C), % 0 to 0.15
0.22 to 0.28
Chromium (Cr), % 12 to 14
0
Iron (Fe), % 83.2 to 87.9
98.7 to 99.18
Manganese (Mn), % 0 to 1.3
0.6 to 0.9
Phosphorus (P), % 0 to 0.060
0 to 0.040
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0.15 to 0.35
0 to 0.050