AISI 416 Stainless Steel vs. SAE-AISI H43 Steel

Both AISI 416 stainless steel and SAE-AISI H43 steel are iron alloys. They have 89% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is AISI 416 stainless steel and the bottom bar is SAE-AISI H43 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
77
Tensile Strength: Ultimate (UTS), MPa 510 to 800
710 to 2140

Thermal Properties

Latent Heat of Fusion, J/g 270
270
Melting Completion (Liquidus), °C 1530
1530
Melting Onset (Solidus), °C 1480
1480
Specific Heat Capacity, J/kg-K 480
460
Thermal Conductivity, W/m-K 30
30
Thermal Expansion, µm/m-K 9.9
12

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
14
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 1.9
8.2
Embodied Energy, MJ/kg 27
120
Embodied Water, L/kg 100
100

Common Calculations

PREN (Pitting Resistance) 13
31
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 18 to 29
25 to 75
Strength to Weight: Bending, points 18 to 25
22 to 46
Thermal Diffusivity, mm2/s 8.1
8.3
Thermal Shock Resistance, points 19 to 30
21 to 62

Alloy Composition

Carbon (C), % 0 to 0.15
0.5 to 0.65
Chromium (Cr), % 12 to 14
3.8 to 4.5
Iron (Fe), % 83.2 to 87.9
83.2 to 85.9
Manganese (Mn), % 0 to 1.3
0.15 to 0.4
Molybdenum (Mo), % 0
7.8 to 8.5
Phosphorus (P), % 0 to 0.060
0 to 0.030
Silicon (Si), % 0 to 1.0
0.2 to 0.45
Sulfur (S), % 0.15 to 0.35
0 to 0.030
Vanadium (V), % 0
1.8 to 2.2