ASTM A182 Grade F12 Class 2 vs. EN 1.0449 Cast Steel

Both ASTM A182 grade F12 class 2 and EN 1.0449 cast steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F12 class 2 and the bottom bar is EN 1.0449 cast steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 22
28
Fatigue Strength, MPa 220
170
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 540
460
Tensile Strength: Yield (Proof), MPa 310
220

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 430
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 43
52
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 2.8
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.6
1.4
Embodied Energy, MJ/kg 21
18
Embodied Water, L/kg 52
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
110
Resilience: Unit (Modulus of Resilience), kJ/m3 260
130
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19
16
Strength to Weight: Bending, points 19
17
Thermal Diffusivity, mm2/s 12
14
Thermal Shock Resistance, points 16
14

Alloy Composition

Carbon (C), % 0.1 to 0.2
0 to 0.18
Chromium (Cr), % 0.8 to 1.3
0
Iron (Fe), % 96.4 to 98.3
98 to 100
Manganese (Mn), % 0.3 to 0.8
0 to 1.2
Molybdenum (Mo), % 0.44 to 0.65
0
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0.1 to 0.6
0 to 0.6
Sulfur (S), % 0 to 0.040
0 to 0.025