EN 1.0449 (GS200) Cast Non-Alloy Steel

EN 1.0449 cast steel is a carbon steel formulated for casting. Cited properties are appropriate for the normalized condition. 1.0449 is the EN numeric designation for this material. GS200 is the EN chemical designation.

It has a fairly high ductility and a fairly low tensile strength among cast carbon steels.

The graph bars on the material properties cards below compare EN 1.0449 cast steel to: cast carbon steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Elastic (Young's, Tensile) Modulus

190 GPa 27 x 106 psi

Elongation at Break

28 %

Fatigue Strength

170 MPa 24 x 103 psi

Impact Strength: V-Notched Charpy

40 J 29 ft-lb

Poisson's Ratio

0.29

Shear Modulus

73 GPa 11 x 106 psi

Tensile Strength: Ultimate (UTS)

460 MPa 66 x 103 psi

Tensile Strength: Yield (Proof)

220 MPa 32 x 103 psi

Thermal Properties

Latent Heat of Fusion

250 J/g

Maximum Temperature: Mechanical

400 °C 750 °F

Melting Completion (Liquidus)

1460 °C 2660 °F

Melting Onset (Solidus)

1420 °C 2590 °F

Specific Heat Capacity

470 J/kg-K 0.11 BTU/lb-°F

Thermal Conductivity

52 W/m-K 30 BTU/h-ft-°F

Thermal Expansion

12 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

7.1 % IACS

Electrical Conductivity: Equal Weight (Specific)

8.1 % IACS

Otherwise Unclassified Properties

Base Metal Price

1.8 % relative

Density

7.8 g/cm3 490 lb/ft3

Embodied Carbon

1.4 kg CO2/kg material

Embodied Energy

18 MJ/kg 7.9 x 103 BTU/lb

Embodied Water

46 L/kg 5.5 gal/lb

Common Calculations

Resilience: Ultimate (Unit Rupture Work)

110 MJ/m3

Resilience: Unit (Modulus of Resilience)

130 kJ/m3

Stiffness to Weight: Axial

13 points

Stiffness to Weight: Bending

24 points

Strength to Weight: Axial

16 points

Strength to Weight: Bending

17 points

Thermal Diffusivity

14 mm2/s

Thermal Shock Resistance

14 points

Alloy Composition

Iron (Fe)Fe 98 to 100
Manganese (Mn)Mn 0 to 1.2
Silicon (Si)Si 0 to 0.6
Carbon (C)C 0 to 0.18
Phosphorus (P)P 0 to 0.030
Sulfur (S)S 0 to 0.025

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Similar Alloys

Further Reading

EN 10293: Steel castings - Steel castings for general engineering uses

Microstructure of Steels and Cast Irons, Madeleine Durand-Charre, 2004

Carbon Steel Handbook, D. Gandy, 2007

ASM Specialty Handbook: Carbon and Alloy Steels, J. R. Davis (editor), 1996

Ferrous Materials: Steel and Cast Iron, Hans Berns and Werner Theisen, 2008

Steels: Processing, Structure, and Performance, 2nd ed., George Krauss, 2015