ASTM A182 Grade F23 vs. AWS BAg-35

ASTM A182 grade F23 belongs to the iron alloys classification, while AWS BAg-35 belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F23 and the bottom bar is AWS BAg-35.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
91
Poisson's Ratio 0.29
0.32
Shear Modulus, GPa 74
34
Tensile Strength: Ultimate (UTS), MPa 570
170

Thermal Properties

Latent Heat of Fusion, J/g 250
140
Melting Completion (Liquidus), °C 1500
750
Melting Onset (Solidus), °C 1450
690
Specific Heat Capacity, J/kg-K 470
330
Thermal Expansion, µm/m-K 13
21

Otherwise Unclassified Properties

Density, g/cm3 8.0
8.7
Embodied Carbon, kg CO2/kg material 2.5
35
Embodied Energy, MJ/kg 36
550

Common Calculations

Stiffness to Weight: Axial, points 13
5.8
Stiffness to Weight: Bending, points 24
17
Strength to Weight: Axial, points 20
5.4
Strength to Weight: Bending, points 19
7.8
Thermal Shock Resistance, points 17
6.4

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.030
0
Boron (B), % 0.0010 to 0.0060
0
Carbon (C), % 0.040 to 0.1
0
Chromium (Cr), % 1.9 to 2.6
0
Copper (Cu), % 0
31 to 33
Iron (Fe), % 93.2 to 96.2
0
Manganese (Mn), % 0.1 to 0.6
0
Molybdenum (Mo), % 0.050 to 0.3
0
Nickel (Ni), % 0 to 0.4
0
Niobium (Nb), % 0.020 to 0.080
0
Nitrogen (N), % 0 to 0.015
0
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 0 to 0.5
0
Silver (Ag), % 0
34 to 36
Sulfur (S), % 0 to 0.010
0
Titanium (Ti), % 0.0050 to 0.060
0
Tungsten (W), % 1.5 to 1.8
0
Vanadium (V), % 0.2 to 0.3
0
Zinc (Zn), % 0
31 to 35
Residuals, % 0
0 to 0.15