ASTM A182 Grade F23 vs. AWS BAu-4

ASTM A182 grade F23 belongs to the iron alloys classification, while AWS BAu-4 belongs to the otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (19, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is ASTM A182 grade F23 and the bottom bar is AWS BAu-4.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
110
Poisson's Ratio 0.29
0.4
Shear Modulus, GPa 74
41
Tensile Strength: Ultimate (UTS), MPa 570
200

Thermal Properties

Latent Heat of Fusion, J/g 250
100
Melting Completion (Liquidus), °C 1500
950
Melting Onset (Solidus), °C 1450
950
Specific Heat Capacity, J/kg-K 470
190
Thermal Expansion, µm/m-K 13
14

Otherwise Unclassified Properties

Density, g/cm3 8.0
17

Common Calculations

Stiffness to Weight: Axial, points 13
3.6
Stiffness to Weight: Bending, points 24
9.3
Strength to Weight: Axial, points 20
3.2
Strength to Weight: Bending, points 19
4.4
Thermal Shock Resistance, points 17
9.2

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.030
0
Boron (B), % 0.0010 to 0.0060
0
Carbon (C), % 0.040 to 0.1
0
Chromium (Cr), % 1.9 to 2.6
0
Gold (Au), % 0
81.5 to 82.5
Iron (Fe), % 93.2 to 96.2
0
Manganese (Mn), % 0.1 to 0.6
0
Molybdenum (Mo), % 0.050 to 0.3
0
Nickel (Ni), % 0 to 0.4
17.4 to 18.5
Niobium (Nb), % 0.020 to 0.080
0
Nitrogen (N), % 0 to 0.015
0
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 0 to 0.5
0
Sulfur (S), % 0 to 0.010
0
Titanium (Ti), % 0.0050 to 0.060
0
Tungsten (W), % 1.5 to 1.8
0
Vanadium (V), % 0.2 to 0.3
0
Residuals, % 0
0 to 0.15