ASTM A182 Grade F23 vs. AWS E2553

Both ASTM A182 grade F23 and AWS E2553 are iron alloys. They have 63% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F23 and the bottom bar is AWS E2553.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 22
17
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 74
80
Tensile Strength: Ultimate (UTS), MPa 570
850

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Melting Completion (Liquidus), °C 1500
1440
Melting Onset (Solidus), °C 1450
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 41
16
Thermal Expansion, µm/m-K 13
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.8
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
21
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 2.5
4.0
Embodied Energy, MJ/kg 36
56
Embodied Water, L/kg 59
190

Common Calculations

PREN (Pitting Resistance) 5.7
40
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 20
30
Strength to Weight: Bending, points 19
26
Thermal Diffusivity, mm2/s 11
4.3
Thermal Shock Resistance, points 17
21

Alloy Composition

Aluminum (Al), % 0 to 0.030
0
Boron (B), % 0.0010 to 0.0060
0
Carbon (C), % 0.040 to 0.1
0 to 0.060
Chromium (Cr), % 1.9 to 2.6
24 to 27
Copper (Cu), % 0
1.5 to 2.5
Iron (Fe), % 93.2 to 96.2
55.2 to 64.5
Manganese (Mn), % 0.1 to 0.6
0.5 to 1.5
Molybdenum (Mo), % 0.050 to 0.3
2.9 to 3.9
Nickel (Ni), % 0 to 0.4
6.5 to 8.5
Niobium (Nb), % 0.020 to 0.080
0
Nitrogen (N), % 0 to 0.015
0.1 to 0.25
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.030
Titanium (Ti), % 0.0050 to 0.060
0
Tungsten (W), % 1.5 to 1.8
0
Vanadium (V), % 0.2 to 0.3
0