ASTM A182 Grade F23 vs. AWS ERNiCrCoMo-1

ASTM A182 grade F23 belongs to the iron alloys classification, while AWS ERNiCrCoMo-1 belongs to the nickel alloys. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F23 and the bottom bar is AWS ERNiCrCoMo-1.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 22
28
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
81
Tensile Strength: Ultimate (UTS), MPa 570
710

Thermal Properties

Latent Heat of Fusion, J/g 250
330
Melting Completion (Liquidus), °C 1500
1420
Melting Onset (Solidus), °C 1450
1370
Specific Heat Capacity, J/kg-K 470
450
Thermal Conductivity, W/m-K 41
13
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.8
1.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
1.5

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
75
Density, g/cm3 8.0
8.5
Embodied Carbon, kg CO2/kg material 2.5
10
Embodied Energy, MJ/kg 36
140
Embodied Water, L/kg 59
350

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 20
23
Strength to Weight: Bending, points 19
21
Thermal Diffusivity, mm2/s 11
3.5
Thermal Shock Resistance, points 17
19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.030
0.8 to 1.5
Boron (B), % 0.0010 to 0.0060
0
Carbon (C), % 0.040 to 0.1
0.050 to 0.15
Chromium (Cr), % 1.9 to 2.6
20 to 24
Cobalt (Co), % 0
10 to 15
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 93.2 to 96.2
0 to 3.0
Manganese (Mn), % 0.1 to 0.6
0 to 1.0
Molybdenum (Mo), % 0.050 to 0.3
8.0 to 10
Nickel (Ni), % 0 to 0.4
42.7 to 61.2
Niobium (Nb), % 0.020 to 0.080
0
Nitrogen (N), % 0 to 0.015
0
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.015
Titanium (Ti), % 0.0050 to 0.060
0 to 0.6
Tungsten (W), % 1.5 to 1.8
0
Vanadium (V), % 0.2 to 0.3
0
Residuals, % 0
0 to 0.5