ASTM A182 Grade F23 vs. EN 1.6773 Steel

Both ASTM A182 grade F23 and EN 1.6773 steel are iron alloys. They have a very high 96% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F23 and the bottom bar is EN 1.6773 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
340
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 22
11
Fatigue Strength, MPa 320
560
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
73
Shear Strength, MPa 360
670
Tensile Strength: Ultimate (UTS), MPa 570
1120
Tensile Strength: Yield (Proof), MPa 460
910

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 450
450
Melting Completion (Liquidus), °C 1500
1460
Melting Onset (Solidus), °C 1450
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 41
46
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.8
8.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
9.2

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
5.0
Density, g/cm3 8.0
7.9
Embodied Carbon, kg CO2/kg material 2.5
1.9
Embodied Energy, MJ/kg 36
26
Embodied Water, L/kg 59
61

Common Calculations

PREN (Pitting Resistance) 5.7
3.0
Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
110
Resilience: Unit (Modulus of Resilience), kJ/m3 550
2210
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 20
40
Strength to Weight: Bending, points 19
30
Thermal Diffusivity, mm2/s 11
12
Thermal Shock Resistance, points 17
33

Alloy Composition

Aluminum (Al), % 0 to 0.030
0
Boron (B), % 0.0010 to 0.0060
0
Carbon (C), % 0.040 to 0.1
0.32 to 0.39
Chromium (Cr), % 1.9 to 2.6
1.6 to 2.0
Iron (Fe), % 93.2 to 96.2
92 to 93.9
Manganese (Mn), % 0.1 to 0.6
0.3 to 0.6
Molybdenum (Mo), % 0.050 to 0.3
0.25 to 0.45
Nickel (Ni), % 0 to 0.4
3.6 to 4.1
Niobium (Nb), % 0.020 to 0.080
0
Nitrogen (N), % 0 to 0.015
0
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0 to 0.5
0 to 0.4
Sulfur (S), % 0 to 0.010
0 to 0.025
Titanium (Ti), % 0.0050 to 0.060
0
Tungsten (W), % 1.5 to 1.8
0
Vanadium (V), % 0.2 to 0.3
0