ASTM A182 Grade F23 vs. EN 1.8062 Steel

Both ASTM A182 grade F23 and EN 1.8062 steel are iron alloys. They have a very high 96% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F23 and the bottom bar is EN 1.8062 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
200 to 510
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
72
Tensile Strength: Ultimate (UTS), MPa 570
660 to 1910

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Maximum Temperature: Mechanical, °C 450
420
Melting Completion (Liquidus), °C 1500
1440
Melting Onset (Solidus), °C 1450
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 41
43
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.8
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
2.4
Density, g/cm3 8.0
7.7
Embodied Carbon, kg CO2/kg material 2.5
1.5
Embodied Energy, MJ/kg 36
20
Embodied Water, L/kg 59
49

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 20
24 to 69
Strength to Weight: Bending, points 19
22 to 44
Thermal Diffusivity, mm2/s 11
12
Thermal Shock Resistance, points 17
20 to 57

Alloy Composition

Aluminum (Al), % 0 to 0.030
0
Boron (B), % 0.0010 to 0.0060
0
Carbon (C), % 0.040 to 0.1
0.42 to 0.5
Chromium (Cr), % 1.9 to 2.6
0.5 to 0.8
Iron (Fe), % 93.2 to 96.2
95.9 to 97.1
Manganese (Mn), % 0.1 to 0.6
0.5 to 0.8
Molybdenum (Mo), % 0.050 to 0.3
0.2 to 0.3
Nickel (Ni), % 0 to 0.4
0
Niobium (Nb), % 0.020 to 0.080
0
Nitrogen (N), % 0 to 0.015
0
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0 to 0.5
1.3 to 1.7
Sulfur (S), % 0 to 0.010
0 to 0.025
Titanium (Ti), % 0.0050 to 0.060
0
Tungsten (W), % 1.5 to 1.8
0
Vanadium (V), % 0.2 to 0.3
0