ASTM A182 Grade F23 vs. EN AC-51100 Aluminum

ASTM A182 grade F23 belongs to the iron alloys classification, while EN AC-51100 aluminum belongs to the aluminum alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is ASTM A182 grade F23 and the bottom bar is EN AC-51100 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
57
Elastic (Young's, Tensile) Modulus, GPa 190
68
Elongation at Break, % 22
4.5
Fatigue Strength, MPa 320
58
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 74
26
Tensile Strength: Ultimate (UTS), MPa 570
160
Tensile Strength: Yield (Proof), MPa 460
80

Thermal Properties

Latent Heat of Fusion, J/g 250
400
Maximum Temperature: Mechanical, °C 450
170
Melting Completion (Liquidus), °C 1500
640
Melting Onset (Solidus), °C 1450
620
Specific Heat Capacity, J/kg-K 470
900
Thermal Conductivity, W/m-K 41
130
Thermal Expansion, µm/m-K 13
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.8
34
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
110

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
9.5
Density, g/cm3 8.0
2.7
Embodied Carbon, kg CO2/kg material 2.5
8.7
Embodied Energy, MJ/kg 36
150
Embodied Water, L/kg 59
1180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
6.0
Resilience: Unit (Modulus of Resilience), kJ/m3 550
47
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
51
Strength to Weight: Axial, points 20
17
Strength to Weight: Bending, points 19
25
Thermal Diffusivity, mm2/s 11
53
Thermal Shock Resistance, points 17
7.3

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.030
94.5 to 97.5
Boron (B), % 0.0010 to 0.0060
0
Carbon (C), % 0.040 to 0.1
0
Chromium (Cr), % 1.9 to 2.6
0
Copper (Cu), % 0
0 to 0.050
Iron (Fe), % 93.2 to 96.2
0 to 0.55
Magnesium (Mg), % 0
2.5 to 3.5
Manganese (Mn), % 0.1 to 0.6
0 to 0.45
Molybdenum (Mo), % 0.050 to 0.3
0
Nickel (Ni), % 0 to 0.4
0
Niobium (Nb), % 0.020 to 0.080
0
Nitrogen (N), % 0 to 0.015
0
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 0 to 0.5
0 to 0.55
Sulfur (S), % 0 to 0.010
0
Titanium (Ti), % 0.0050 to 0.060
0 to 0.2
Tungsten (W), % 1.5 to 1.8
0
Vanadium (V), % 0.2 to 0.3
0
Zinc (Zn), % 0
0 to 0.1
Residuals, % 0
0 to 0.15