ASTM A182 Grade F23 vs. Grade 702C Zirconium

ASTM A182 grade F23 belongs to the iron alloys classification, while grade 702C zirconium belongs to the otherwise unclassified metals. There are 21 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F23 and the bottom bar is grade 702C zirconium.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
180
Elastic (Young's, Tensile) Modulus, GPa 190
97
Elongation at Break, % 22
13
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 74
36
Tensile Strength: Ultimate (UTS), MPa 570
430
Tensile Strength: Yield (Proof), MPa 460
310

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Specific Heat Capacity, J/kg-K 470
270
Thermal Conductivity, W/m-K 41
22
Thermal Expansion, µm/m-K 13
5.7

Otherwise Unclassified Properties

Density, g/cm3 8.0
6.7
Embodied Water, L/kg 59
450

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
52
Resilience: Unit (Modulus of Resilience), kJ/m3 550
510
Stiffness to Weight: Axial, points 13
8.1
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 20
18
Strength to Weight: Bending, points 19
19
Thermal Diffusivity, mm2/s 11
12
Thermal Shock Resistance, points 17
55

Alloy Composition

Aluminum (Al), % 0 to 0.030
0
Boron (B), % 0.0010 to 0.0060
0
Carbon (C), % 0.040 to 0.1
0 to 0.1
Chromium (Cr), % 1.9 to 2.6
0
Hafnium (Hf), % 0
0 to 4.5
Hydrogen (H), % 0
0 to 0.0050
Iron (Fe), % 93.2 to 96.2
0 to 0.3
Manganese (Mn), % 0.1 to 0.6
0
Molybdenum (Mo), % 0.050 to 0.3
0
Nickel (Ni), % 0 to 0.4
0
Niobium (Nb), % 0.020 to 0.080
0
Nitrogen (N), % 0 to 0.015
0 to 0.030
Oxygen (O), % 0
0 to 0.25
Phosphorus (P), % 0 to 0.030
0 to 0.010
Silicon (Si), % 0 to 0.5
0
Sulfur (S), % 0 to 0.010
0
Titanium (Ti), % 0.0050 to 0.060
0
Tungsten (W), % 1.5 to 1.8
0
Vanadium (V), % 0.2 to 0.3
0
Zirconium (Zr), % 0
94.8 to 100