ASTM A182 Grade F23 vs. C16200 Copper
ASTM A182 grade F23 belongs to the iron alloys classification, while C16200 copper belongs to the copper alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is ASTM A182 grade F23 and the bottom bar is C16200 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 120 |
| Elongation at Break, % | 22 | |
| 2.0 to 56 |
| Fatigue Strength, MPa | 320 | |
| 100 to 210 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 74 | |
| 43 |
| Shear Strength, MPa | 360 | |
| 190 to 390 |
| Tensile Strength: Ultimate (UTS), MPa | 570 | |
| 240 to 550 |
| Tensile Strength: Yield (Proof), MPa | 460 | |
| 48 to 470 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 450 | |
| 370 |
| Melting Completion (Liquidus), °C | 1500 | |
| 1080 |
| Melting Onset (Solidus), °C | 1450 | |
| 1030 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 380 |
| Thermal Conductivity, W/m-K | 41 | |
| 360 |
| Thermal Expansion, µm/m-K | 13 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.8 | |
| 90 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.9 | |
| 90 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 7.0 | |
| 30 |
| Density, g/cm3 | 8.0 | |
| 9.0 |
| Embodied Carbon, kg CO2/kg material | 2.5 | |
| 2.6 |
| Embodied Energy, MJ/kg | 36 | |
| 41 |
| Embodied Water, L/kg | 59 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 120 | |
| 10 to 99 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 550 | |
| 10 to 970 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 24 | |
| 18 |
| Strength to Weight: Axial, points | 20 | |
| 7.4 to 17 |
| Strength to Weight: Bending, points | 19 | |
| 9.6 to 17 |
| Thermal Diffusivity, mm2/s | 11 | |
| 100 |
| Thermal Shock Resistance, points | 17 | |
| 8.7 to 20 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.030 | |
| 0 |
| Boron (B), % | 0.0010 to 0.0060 | |
| 0 |
| Cadmium (Cd), % | 0 | |
| 0.7 to 1.2 |
| Carbon (C), % | 0.040 to 0.1 | |
| 0 |
| Chromium (Cr), % | 1.9 to 2.6 | |
| 0 |
| Copper (Cu), % | 0 | |
| 98.6 to 99.3 |
| Iron (Fe), % | 93.2 to 96.2 | |
| 0 to 0.2 |
| Manganese (Mn), % | 0.1 to 0.6 | |
| 0 |
| Molybdenum (Mo), % | 0.050 to 0.3 | |
| 0 |
| Nickel (Ni), % | 0 to 0.4 | |
| 0 |
| Niobium (Nb), % | 0.020 to 0.080 | |
| 0 |
| Nitrogen (N), % | 0 to 0.015 | |
| 0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 |
| Titanium (Ti), % | 0.0050 to 0.060 | |
| 0 |
| Tungsten (W), % | 1.5 to 1.8 | |
| 0 |
| Vanadium (V), % | 0.2 to 0.3 | |
| 0 |