ASTM A182 Grade F23 vs. S20433 Stainless Steel

Both ASTM A182 grade F23 and S20433 stainless steel are iron alloys. They have 71% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F23 and the bottom bar is S20433 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
190
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 22
46
Fatigue Strength, MPa 320
250
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
76
Shear Strength, MPa 360
440
Tensile Strength: Ultimate (UTS), MPa 570
630
Tensile Strength: Yield (Proof), MPa 460
270

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 450
900
Melting Completion (Liquidus), °C 1500
1400
Melting Onset (Solidus), °C 1450
1360
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 41
15
Thermal Expansion, µm/m-K 13
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.8
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
2.8

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
13
Density, g/cm3 8.0
7.7
Embodied Carbon, kg CO2/kg material 2.5
2.7
Embodied Energy, MJ/kg 36
39
Embodied Water, L/kg 59
150

Common Calculations

PREN (Pitting Resistance) 5.7
20
Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
230
Resilience: Unit (Modulus of Resilience), kJ/m3 550
180
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 20
23
Strength to Weight: Bending, points 19
21
Thermal Diffusivity, mm2/s 11
4.0
Thermal Shock Resistance, points 17
14

Alloy Composition

Aluminum (Al), % 0 to 0.030
0
Boron (B), % 0.0010 to 0.0060
0
Carbon (C), % 0.040 to 0.1
0 to 0.080
Chromium (Cr), % 1.9 to 2.6
17 to 18
Copper (Cu), % 0
1.5 to 3.5
Iron (Fe), % 93.2 to 96.2
64.1 to 72.4
Manganese (Mn), % 0.1 to 0.6
5.5 to 7.5
Molybdenum (Mo), % 0.050 to 0.3
0
Nickel (Ni), % 0 to 0.4
3.5 to 5.5
Niobium (Nb), % 0.020 to 0.080
0
Nitrogen (N), % 0 to 0.015
0.1 to 0.25
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 0 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.030
Titanium (Ti), % 0.0050 to 0.060
0
Tungsten (W), % 1.5 to 1.8
0
Vanadium (V), % 0.2 to 0.3
0