ASTM A182 Grade F23 vs. Z41121 Zinc

ASTM A182 grade F23 belongs to the iron alloys classification, while Z41121 zinc belongs to the zinc alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F23 and the bottom bar is Z41121 zinc.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
87
Elongation at Break, % 22
50
Poisson's Ratio 0.29
0.25
Shear Modulus, GPa 74
35
Tensile Strength: Ultimate (UTS), MPa 570
140
Tensile Strength: Yield (Proof), MPa 460
120

Thermal Properties

Latent Heat of Fusion, J/g 250
110
Maximum Temperature: Mechanical, °C 450
90
Melting Completion (Liquidus), °C 1500
410
Melting Onset (Solidus), °C 1450
400
Specific Heat Capacity, J/kg-K 470
390
Thermal Conductivity, W/m-K 41
110
Thermal Expansion, µm/m-K 13
26

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.8
27
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
37

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
11
Density, g/cm3 8.0
6.6
Embodied Carbon, kg CO2/kg material 2.5
2.8
Embodied Energy, MJ/kg 36
54
Embodied Water, L/kg 59
340

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
68
Resilience: Unit (Modulus of Resilience), kJ/m3 550
79
Stiffness to Weight: Axial, points 13
7.4
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 20
6.1
Strength to Weight: Bending, points 19
9.3
Thermal Diffusivity, mm2/s 11
44
Thermal Shock Resistance, points 17
4.6

Alloy Composition

Aluminum (Al), % 0 to 0.030
0 to 0.010
Boron (B), % 0.0010 to 0.0060
0
Cadmium (Cd), % 0
0 to 0.0050
Carbon (C), % 0.040 to 0.1
0
Chromium (Cr), % 1.9 to 2.6
0
Copper (Cu), % 0
0.080 to 0.49
Iron (Fe), % 93.2 to 96.2
0 to 0.010
Lead (Pb), % 0
0 to 0.010
Manganese (Mn), % 0.1 to 0.6
0
Molybdenum (Mo), % 0.050 to 0.3
0
Nickel (Ni), % 0 to 0.4
0
Niobium (Nb), % 0.020 to 0.080
0
Nitrogen (N), % 0 to 0.015
0
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 0 to 0.5
0
Sulfur (S), % 0 to 0.010
0
Tin (Sn), % 0
0 to 0.0030
Titanium (Ti), % 0.0050 to 0.060
0.050 to 0.18
Tungsten (W), % 1.5 to 1.8
0
Vanadium (V), % 0.2 to 0.3
0
Zinc (Zn), % 0
99.292 to 99.87