ASTM A182 Grade F24 vs. EN 1.0034 Steel

Both ASTM A182 grade F24 and EN 1.0034 steel are iron alloys. They have a very high 96% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F24 and the bottom bar is EN 1.0034 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
97 to 110
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23
9.0 to 32
Fatigue Strength, MPa 330
140 to 170
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
73
Shear Strength, MPa 420
220 to 230
Tensile Strength: Ultimate (UTS), MPa 670
340 to 380
Tensile Strength: Yield (Proof), MPa 460
180 to 280

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Maximum Temperature: Mechanical, °C 460
400
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
53
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.8
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 4.0
1.8
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 2.3
1.4
Embodied Energy, MJ/kg 33
18
Embodied Water, L/kg 61
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
31 to 95
Resilience: Unit (Modulus of Resilience), kJ/m3 570
84 to 210
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 24
12 to 13
Strength to Weight: Bending, points 22
14 to 15
Thermal Diffusivity, mm2/s 11
14
Thermal Shock Resistance, points 19
11 to 12

Alloy Composition

Aluminum (Al), % 0 to 0.020
0
Boron (B), % 0.0015 to 0.0070
0
Carbon (C), % 0.050 to 0.1
0 to 0.15
Chromium (Cr), % 2.2 to 2.6
0
Iron (Fe), % 94.5 to 96.1
98.7 to 100
Manganese (Mn), % 0.3 to 0.7
0 to 0.7
Molybdenum (Mo), % 0.9 to 1.1
0
Nitrogen (N), % 0 to 0.12
0
Phosphorus (P), % 0 to 0.020
0 to 0.045
Silicon (Si), % 0.15 to 0.45
0 to 0.35
Sulfur (S), % 0 to 0.010
0 to 0.045
Titanium (Ti), % 0.060 to 0.1
0
Vanadium (V), % 0.2 to 0.3
0