ASTM A182 Grade F36 vs. SAE-AISI H43 Steel

Both ASTM A182 grade F36 and SAE-AISI H43 steel are iron alloys. They have 86% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F36 and the bottom bar is SAE-AISI H43 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
77
Tensile Strength: Ultimate (UTS), MPa 710
710 to 2140

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Melting Completion (Liquidus), °C 1460
1530
Melting Onset (Solidus), °C 1420
1480
Specific Heat Capacity, J/kg-K 470
460
Thermal Conductivity, W/m-K 39
30
Thermal Expansion, µm/m-K 13
12

Otherwise Unclassified Properties

Base Metal Price, % relative 3.4
14
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 1.7
8.2
Embodied Energy, MJ/kg 22
120
Embodied Water, L/kg 53
100

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25
25 to 75
Strength to Weight: Bending, points 22
22 to 46
Thermal Diffusivity, mm2/s 10
8.3
Thermal Shock Resistance, points 21
21 to 62

Alloy Composition

Aluminum (Al), % 0 to 0.050
0
Carbon (C), % 0.1 to 0.17
0.5 to 0.65
Chromium (Cr), % 0 to 0.3
3.8 to 4.5
Copper (Cu), % 0.5 to 0.8
0
Iron (Fe), % 95 to 97.1
83.2 to 85.9
Manganese (Mn), % 0.8 to 1.2
0.15 to 0.4
Molybdenum (Mo), % 0.25 to 0.5
7.8 to 8.5
Nickel (Ni), % 1.0 to 1.3
0
Niobium (Nb), % 0.015 to 0.045
0
Nitrogen (N), % 0 to 0.020
0
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0.25 to 0.5
0.2 to 0.45
Sulfur (S), % 0 to 0.025
0 to 0.030
Vanadium (V), % 0 to 0.020
1.8 to 2.2