ASTM A182 Grade F3VCb vs. EN 1.3961 Alloy

Both ASTM A182 grade F3VCb and EN 1.3961 alloy are iron alloys. They have 64% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F3VCb and the bottom bar is EN 1.3961 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 21
31
Poisson's Ratio 0.29
0.3
Shear Modulus, GPa 74
72
Shear Strength, MPa 420
300
Tensile Strength: Ultimate (UTS), MPa 670
450
Tensile Strength: Yield (Proof), MPa 460
310

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Melting Completion (Liquidus), °C 1470
1430
Melting Onset (Solidus), °C 1430
1390
Specific Heat Capacity, J/kg-K 470
460
Thermal Expansion, µm/m-K 13
1.3

Otherwise Unclassified Properties

Base Metal Price, % relative 4.5
25
Density, g/cm3 7.9
8.2
Embodied Carbon, kg CO2/kg material 2.4
4.8
Embodied Energy, MJ/kg 33
66
Embodied Water, L/kg 64
110

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
130
Resilience: Unit (Modulus of Resilience), kJ/m3 570
250
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 24
15
Strength to Weight: Bending, points 22
16
Thermal Shock Resistance, points 19
130

Alloy Composition

Calcium (Ca), % 0.00050 to 0.015
0
Carbon (C), % 0.1 to 0.15
0 to 0.050
Chromium (Cr), % 2.7 to 3.3
0 to 0.25
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 93.8 to 95.8
60.7 to 65
Manganese (Mn), % 0.3 to 0.6
0 to 0.5
Molybdenum (Mo), % 0.9 to 1.1
0 to 1.0
Nickel (Ni), % 0 to 0.25
35 to 37
Niobium (Nb), % 0.015 to 0.070
0
Phosphorus (P), % 0 to 0.020
0 to 0.030
Silicon (Si), % 0 to 0.1
0 to 0.5
Sulfur (S), % 0 to 0.010
0 to 0.020
Titanium (Ti), % 0 to 0.015
0
Vanadium (V), % 0.2 to 0.3
0