ASTM A182 Grade F3VCb vs. EN 1.4587 Stainless Steel

Both ASTM A182 grade F3VCb and EN 1.4587 stainless steel are iron alloys. They have 42% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F3VCb and the bottom bar is EN 1.4587 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
160
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 21
34
Fatigue Strength, MPa 320
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
80
Tensile Strength: Ultimate (UTS), MPa 670
540
Tensile Strength: Yield (Proof), MPa 460
250

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Maximum Temperature: Mechanical, °C 470
1100
Melting Completion (Liquidus), °C 1470
1420
Melting Onset (Solidus), °C 1430
1370
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 40
17
Thermal Expansion, µm/m-K 13
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.7
1.8
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
2.0

Otherwise Unclassified Properties

Base Metal Price, % relative 4.5
36
Density, g/cm3 7.9
8.1
Embodied Carbon, kg CO2/kg material 2.4
6.3
Embodied Energy, MJ/kg 33
87
Embodied Water, L/kg 64
230

Common Calculations

PREN (Pitting Resistance) 6.3
43
Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
150
Resilience: Unit (Modulus of Resilience), kJ/m3 570
150
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 24
18
Strength to Weight: Bending, points 22
18
Thermal Diffusivity, mm2/s 11
4.5
Thermal Shock Resistance, points 19
13

Alloy Composition

Calcium (Ca), % 0.00050 to 0.015
0
Carbon (C), % 0.1 to 0.15
0 to 0.030
Chromium (Cr), % 2.7 to 3.3
24 to 26
Copper (Cu), % 0 to 0.25
2.0 to 3.0
Iron (Fe), % 93.8 to 95.8
32.7 to 41.9
Manganese (Mn), % 0.3 to 0.6
0 to 2.0
Molybdenum (Mo), % 0.9 to 1.1
4.0 to 5.0
Nickel (Ni), % 0 to 0.25
28 to 30
Niobium (Nb), % 0.015 to 0.070
0
Nitrogen (N), % 0
0.15 to 0.25
Phosphorus (P), % 0 to 0.020
0 to 0.035
Silicon (Si), % 0 to 0.1
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.025
Titanium (Ti), % 0 to 0.015
0
Vanadium (V), % 0.2 to 0.3
0