ASTM A182 Grade F3VCb vs. EN 1.4855 Stainless Steel

Both ASTM A182 grade F3VCb and EN 1.4855 stainless steel are iron alloys. They have 51% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F3VCb and the bottom bar is EN 1.4855 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
150
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 21
4.6
Fatigue Strength, MPa 320
120
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
77
Tensile Strength: Ultimate (UTS), MPa 670
500
Tensile Strength: Yield (Proof), MPa 460
250

Thermal Properties

Latent Heat of Fusion, J/g 250
320
Maximum Temperature: Mechanical, °C 470
1050
Melting Completion (Liquidus), °C 1470
1400
Melting Onset (Solidus), °C 1430
1350
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 40
14
Thermal Expansion, µm/m-K 13
16

Otherwise Unclassified Properties

Base Metal Price, % relative 4.5
34
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 2.4
5.9
Embodied Energy, MJ/kg 33
85
Embodied Water, L/kg 64
200

Common Calculations

PREN (Pitting Resistance) 6.3
25
Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
19
Resilience: Unit (Modulus of Resilience), kJ/m3 570
160
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 24
18
Strength to Weight: Bending, points 22
18
Thermal Diffusivity, mm2/s 11
3.7
Thermal Shock Resistance, points 19
11

Alloy Composition

Calcium (Ca), % 0.00050 to 0.015
0
Carbon (C), % 0.1 to 0.15
0.3 to 0.5
Chromium (Cr), % 2.7 to 3.3
23 to 25
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 93.8 to 95.8
42.6 to 51.9
Manganese (Mn), % 0.3 to 0.6
0 to 2.0
Molybdenum (Mo), % 0.9 to 1.1
0 to 0.5
Nickel (Ni), % 0 to 0.25
23 to 25
Niobium (Nb), % 0.015 to 0.070
0.8 to 1.8
Phosphorus (P), % 0 to 0.020
0 to 0.040
Silicon (Si), % 0 to 0.1
1.0 to 2.5
Sulfur (S), % 0 to 0.010
0 to 0.030
Titanium (Ti), % 0 to 0.015
0
Vanadium (V), % 0.2 to 0.3
0