ASTM A182 Grade F3VCb vs. EN 1.4941 Stainless Steel

Both ASTM A182 grade F3VCb and EN 1.4941 stainless steel are iron alloys. They have 73% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F3VCb and the bottom bar is EN 1.4941 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
180
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 21
39
Fatigue Strength, MPa 320
180
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
77
Shear Strength, MPa 420
400
Tensile Strength: Ultimate (UTS), MPa 670
590
Tensile Strength: Yield (Proof), MPa 460
210

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 470
940
Melting Completion (Liquidus), °C 1470
1430
Melting Onset (Solidus), °C 1430
1380
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 40
16
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.7
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
2.8

Otherwise Unclassified Properties

Base Metal Price, % relative 4.5
16
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 2.4
3.3
Embodied Energy, MJ/kg 33
47
Embodied Water, L/kg 64
140

Common Calculations

PREN (Pitting Resistance) 6.3
18
Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
180
Resilience: Unit (Modulus of Resilience), kJ/m3 570
110
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 24
21
Strength to Weight: Bending, points 22
20
Thermal Diffusivity, mm2/s 11
4.3
Thermal Shock Resistance, points 19
13

Alloy Composition

Boron (B), % 0
0.0015 to 0.0050
Calcium (Ca), % 0.00050 to 0.015
0
Carbon (C), % 0.1 to 0.15
0.040 to 0.080
Chromium (Cr), % 2.7 to 3.3
17 to 19
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 93.8 to 95.8
65.1 to 73.6
Manganese (Mn), % 0.3 to 0.6
0 to 2.0
Molybdenum (Mo), % 0.9 to 1.1
0
Nickel (Ni), % 0 to 0.25
9.0 to 12
Niobium (Nb), % 0.015 to 0.070
0
Phosphorus (P), % 0 to 0.020
0 to 0.035
Silicon (Si), % 0 to 0.1
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.015
Titanium (Ti), % 0 to 0.015
0.4 to 0.8
Vanadium (V), % 0.2 to 0.3
0