ASTM A202 Steel vs. AISI 422 Stainless Steel

Both ASTM A202 steel and AISI 422 stainless steel are iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ASTM A202 steel and the bottom bar is AISI 422 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180 to 200
260 to 330
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 17 to 18
15 to 17
Fatigue Strength, MPa 240
410 to 500
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Shear Strength, MPa 360 to 410
560 to 660
Tensile Strength: Ultimate (UTS), MPa 590 to 670
910 to 1080
Tensile Strength: Yield (Proof), MPa 350 to 360
670 to 870

Thermal Properties

Latent Heat of Fusion, J/g 260
270
Maximum Temperature: Mechanical, °C 410
650
Melting Completion (Liquidus), °C 1450
1480
Melting Onset (Solidus), °C 1410
1470
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 52
24
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
4.7
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
5.3

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
11
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.4
3.1
Embodied Energy, MJ/kg 19
44
Embodied Water, L/kg 49
100

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 93 to 96
140 to 150
Resilience: Unit (Modulus of Resilience), kJ/m3 330 to 350
1140 to 1910
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 21 to 24
32 to 38
Strength to Weight: Bending, points 20 to 22
26 to 30
Thermal Diffusivity, mm2/s 14
6.4
Thermal Shock Resistance, points 17 to 20
33 to 39

Comparable Variants