ASTM A202 Steel vs. EN 1.4565 Stainless Steel

Both ASTM A202 steel and EN 1.4565 stainless steel are iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ASTM A202 steel and the bottom bar is EN 1.4565 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 17 to 18
35
Fatigue Strength, MPa 240
380
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
81
Shear Strength, MPa 360 to 410
590
Tensile Strength: Ultimate (UTS), MPa 590 to 670
880
Tensile Strength: Yield (Proof), MPa 350 to 360
480

Thermal Properties

Latent Heat of Fusion, J/g 260
310
Maximum Temperature: Mechanical, °C 410
1100
Melting Completion (Liquidus), °C 1450
1420
Melting Onset (Solidus), °C 1410
1380
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 52
12
Thermal Expansion, µm/m-K 13
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
1.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
2.1

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
28
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.4
5.4
Embodied Energy, MJ/kg 19
74
Embodied Water, L/kg 49
210

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 93 to 96
260
Resilience: Unit (Modulus of Resilience), kJ/m3 330 to 350
550
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 21 to 24
31
Strength to Weight: Bending, points 20 to 22
26
Thermal Diffusivity, mm2/s 14
3.2
Thermal Shock Resistance, points 17 to 20
21