ASTM A204 Steel vs. EN 1.4434 Stainless Steel

Both ASTM A204 steel and EN 1.4434 stainless steel are iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM A204 steel and the bottom bar is EN 1.4434 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160 to 180
200
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 18 to 22
41
Fatigue Strength, MPa 200 to 220
270
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
79
Shear Strength, MPa 330 to 360
450
Tensile Strength: Ultimate (UTS), MPa 520 to 590
660
Tensile Strength: Yield (Proof), MPa 290 to 330
310

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 410
980
Melting Completion (Liquidus), °C 1470
1450
Melting Onset (Solidus), °C 1420 to 1430
1400
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 52
15
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
21
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 1.5
4.2
Embodied Energy, MJ/kg 20
57
Embodied Water, L/kg 47
160

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 90 to 95
220
Resilience: Unit (Modulus of Resilience), kJ/m3 220 to 290
240
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 18 to 21
23
Strength to Weight: Bending, points 18 to 20
21
Thermal Diffusivity, mm2/s 14
4.0
Thermal Shock Resistance, points 15 to 17
15