ASTM A204 Steel vs. SAE-AISI H14 Steel

Both ASTM A204 steel and SAE-AISI H14 steel are iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is ASTM A204 steel and the bottom bar is SAE-AISI H14 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
75
Tensile Strength: Ultimate (UTS), MPa 520 to 590
710 to 2030

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Melting Completion (Liquidus), °C 1470
1530
Melting Onset (Solidus), °C 1420 to 1430
1490
Specific Heat Capacity, J/kg-K 470
460
Thermal Conductivity, W/m-K 52
35
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
9.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
10

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
15
Density, g/cm3 7.9
8.1
Embodied Carbon, kg CO2/kg material 1.5
2.7
Embodied Energy, MJ/kg 20
39
Embodied Water, L/kg 47
73

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 18 to 21
24 to 69
Strength to Weight: Bending, points 18 to 20
22 to 44
Thermal Diffusivity, mm2/s 14
9.3
Thermal Shock Resistance, points 15 to 17
24 to 68