ASTM A27 Cast Steel vs. EN 1.4421 Stainless Steel

Both ASTM A27 cast steel and EN 1.4421 stainless steel are iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ASTM A27 cast steel and the bottom bar is EN 1.4421 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 25 to 27
11 to 17
Fatigue Strength, MPa 170 to 230
380 to 520
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Tensile Strength: Ultimate (UTS), MPa 460 to 550
880 to 1100
Tensile Strength: Yield (Proof), MPa 230 to 310
620 to 950

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 400
870
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 52
16
Thermal Expansion, µm/m-K 12
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0 to 7.1
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
12
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
2.6
Embodied Energy, MJ/kg 18
36
Embodied Water, L/kg 45 to 46
130

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 96 to 120
120 to 140
Resilience: Unit (Modulus of Resilience), kJ/m3 140 to 260
960 to 2270
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 16 to 20
31 to 39
Strength to Weight: Bending, points 17 to 19
26 to 30
Thermal Diffusivity, mm2/s 14
4.4
Thermal Shock Resistance, points 15 to 18
31 to 39