ASTM A369 Grade FP5 vs. EN 1.4511 Stainless Steel

Both ASTM A369 grade FP5 and EN 1.4511 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 87% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FP5 and the bottom bar is EN 1.4511 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
180
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 20
25
Fatigue Strength, MPa 160
180
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
77
Shear Strength, MPa 300
330
Tensile Strength: Ultimate (UTS), MPa 470
510
Tensile Strength: Yield (Proof), MPa 240
260

Thermal Properties

Latent Heat of Fusion, J/g 260
280
Maximum Temperature: Mechanical, °C 510
870
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 40
25
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.0
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 9.2
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 4.3
11
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.7
2.5
Embodied Energy, MJ/kg 23
37
Embodied Water, L/kg 69
120

Common Calculations

PREN (Pitting Resistance) 6.8
17
Resilience: Ultimate (Unit Rupture Work), MJ/m3 80
110
Resilience: Unit (Modulus of Resilience), kJ/m3 140
170
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 17
18
Strength to Weight: Bending, points 17
18
Thermal Diffusivity, mm2/s 11
6.7
Thermal Shock Resistance, points 13
19

Alloy Composition

Carbon (C), % 0 to 0.15
0 to 0.050
Chromium (Cr), % 4.0 to 6.0
16 to 18
Iron (Fe), % 92.1 to 95.3
78.9 to 84
Manganese (Mn), % 0.3 to 0.6
0 to 1.0
Molybdenum (Mo), % 0.45 to 0.65
0
Niobium (Nb), % 0
0 to 1.0
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.015