EN 1.4511 (X3CrNb17) Stainless Steel

EN 1.4511 stainless steel is a ferritic stainless steel formulated for primary forming into wrought products. Cited properties are appropriate for the annealed condition. 1.4511 is the EN numeric designation for this material. X3CrNb17 is the EN chemical designation.

It has a moderately high ductility among the wrought ferritic stainless steels in the database.

The graph bars on the material properties cards below compare EN 1.4511 stainless steel to: wrought ferritic stainless steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Brinell Hardness

180

Elastic (Young's, Tensile) Modulus

200 GPa 28 x 106 psi

Elongation at Break

25 %

Fatigue Strength

180 MPa 26 x 103 psi

Poisson's Ratio

0.28

Shear Modulus

77 GPa 11 x 106 psi

Shear Strength

330 MPa 48 x 103 psi

Tensile Strength: Ultimate (UTS)

510 MPa 74 x 103 psi

Tensile Strength: Yield (Proof)

260 MPa 37 x 103 psi

Thermal Properties

Latent Heat of Fusion

280 J/g

Maximum Temperature: Corrosion

480 °C 890 °F

Maximum Temperature: Mechanical

870 °C 1590 °F

Melting Completion (Liquidus)

1440 °C 2630 °F

Melting Onset (Solidus)

1400 °C 2550 °F

Specific Heat Capacity

480 J/kg-K 0.11 BTU/lb-°F

Thermal Conductivity

25 W/m-K 14 BTU/h-ft-°F

Thermal Expansion

10 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

2.9 % IACS

Electrical Conductivity: Equal Weight (Specific)

3.3 % IACS

Otherwise Unclassified Properties

Base Metal Price

11 % relative

Density

7.7 g/cm3 480 lb/ft3

Embodied Carbon

2.5 kg CO2/kg material

Embodied Energy

37 MJ/kg 16 x 103 BTU/lb

Embodied Water

120 L/kg 14 gal/lb

Common Calculations

PREN (Pitting Resistance)

17

Resilience: Ultimate (Unit Rupture Work)

110 MJ/m3

Resilience: Unit (Modulus of Resilience)

170 kJ/m3

Stiffness to Weight: Axial

14 points

Stiffness to Weight: Bending

25 points

Strength to Weight: Axial

18 points

Strength to Weight: Bending

18 points

Thermal Diffusivity

6.7 mm2/s

Thermal Shock Resistance

19 points

Alloy Composition

Among wrought stainless steels, the composition of EN 1.4511 stainless steel is notable for including niobium (Nb). Niobium is primarily used to improve yield strength, particularly at elevated temperatures.

Iron (Fe) 78.9 to 84
Chromium (Cr) 16 to 18
Manganese (Mn) 0 to 1.0
Silicon (Si) 0 to 1.0
Niobium (Nb) 0 to 1.0
Carbon (C) 0 to 0.050
Phosphorus (P) 0 to 0.040
Sulfur (S) 0 to 0.015

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Similar Alloys

Further Reading

EN 10088-2: Stainless steels - Part 2: Technical delivery conditions for sheet/plate and strip of corrosion resisting steels for general purposes

EN 10088-3: Stainless steels - Part 3: Technical delivery conditions for semi-finished products, bars, rods, wire, sections and bright products of corrosion resisting steels for general purposes

EN 10088-1: Stainless steels - Part 1: List of stainless steels

Welding Metallurgy of Stainless Steels, Erich Folkhard et al., 2012

Corrosion of Stainless Steels, A. John Sedriks, 1996

Advances in Stainless Steels, Baldev Raj et al. (editors), 2010